A hollow optical fiber 10 has an intermed ate dielectric layer 12
interposed between an inner periphery side dielectric layer 11 facing a
hollow core portion 10a and a metal layer 13. The inner periphery side
dielectric layer 11 is formed of calcium fluoride. The intermediate
dielectric layer 12 is formed of yttrium fluoride. Metal of the metal
layer 13 can be prevented from dispersing into the dielectric layers 12,
11 by the intermediate dielectric layer 12 formed of yttrium fluoride. The
hollow optical fiber 10 is manufactured by vapor depositing calcium
fluoride on an outer peripheral surface of an acid-soluble glass tube 20
(base material), then vapor depositing yttrium fluoride on its outer
peripheral surface, then vapor depositing a metal layer formed of silver,
gold or the like on its outer peripheral surface, and thereafter,
dissolving the glass tube 20 with acid.
Une fibre optique creuse 10 a intermed a mangé la couche diélectrique 12 interposée entre une couche diélectrique 11 de côté intérieur de périphérie faisant face à une partie creuse 10a de noyau et une couche 13 en métal. La couche diélectrique 11 de côté intérieur de périphérie est constituée du fluorure de calcium. La couche diélectrique intermédiaire 12 est constituée du fluorure de yttrium. Le métal de la couche 13 en métal peut être empêché de la dispersion dans les couches diélectriques 12, 11 par la couche diélectrique intermédiaire 12 constituée du fluorure de yttrium. La fibre optique creuse 10 est fabriquée par le fluorure déposant de calcium de vapeur sur une surface périphérique externe d'un tube de verre soluble dans l'acide 20 (matière première), puis vaporise le fluorure déposant de yttrium sur son surface périphérique externe, puis vapeur déposant une couche en métal constituée de l'argent, de l'or ou analogues sur son surface périphérique externe, et ensuite, dissolvant le tube de verre 20 avec de l'acide.