A stainless steel alloy that exhibits both high strength and toughness as a
result of having particular ranges for chemistry, tempering temperatures
and grain size. The alloy is a precipitation-hardened martensitic
stainless steel with an ultimate tensile strength of at least 1200 MPa, a
Charpy impact toughness of greater than 55 J, and a grain size of ASTM 5
or finer. The alloy consists essentially of, by weight, 14.0 to 16.0
percent chromium, 6.0 to 7.0 percent nickel, 1.25 to 1.75 percent copper,
0.5 to 1.0 percent molybdenum, 0.03 to 0.5 percent carbon, niobium in an
amount by weight of ten to twenty times greater than carbon, the balance
iron, minor alloying constituents and impurities.
Uma liga do aço inoxidável que exiba a força elevada e o toughness em conseqüência de ter escalas particulares para o chemistry, temperaturas moderando e tamanho de grão. A liga é um aço inoxidável martensitic precipitação-endurecido com uma força tensile final ao menos de MPa 1200, um toughness do impacto de Charpy mais extremamente de de 55 J, e um tamanho de grão de ASTM 5 ou mais fino. A liga consiste essencialmente em, pelo peso, 14.0 a 16.0 por cento de cromo, 6.0 a 7.0 por cento niquelar, 1.25 a 1.75 por cento de cobre, 0.5 a 1.0 por cento de molibdênio, 0.03 a 0.5 por cento de carbono, niobium em uma quantidade por um peso dez a vinte vezes de mais grande do que o carbono, o ferro do contrapeso, constituents alloying menores e impurezas.