A make-and-break contact material which is less worn out and is able to
achieve an increased life compared to a conventional material of
Ag--CdO-based alloy, in an AC general relay used for a resistive load of
about 1 to 20A in a range of AC 100V to 250V. In the present invention,
the make-and-break contact material of Ag--Ni-based alloy used for a
switching part performing electrical switching through mechanical
switching operation is the make-and-break contact material of Ag--Ni-based
alloy with Ni metal particles dispersed therein which is obtained through
mixing and stirring 3.1 to 20.0 wt % of Ni powder, a certain amount of
Li.sub.2 CO.sub.3 powder corresponding to 0.01 to 0.50 wt % of metal Li as
an additive, and a balance being Ag powder to make a mixture with the
above described powders uniformly dispersed therein, and through
compacting and sintering the above described mixture.
Hacer-y-rompa el material del contacto que se usa menos hacia fuera y puede alcanzar una vida creciente comparada a un material convencional de AG -- aleación CdO-basada, en un relais general de la CA usado para una carga resistente de cerca de 1 a 20A en una gama de la CA 100V a 250V. En la actual invención, hacer-y-rompa el material del contacto de AG -- aleación Ni-basada usada para una pieza de la conmutación la ejecución de la conmutación eléctrica con la operación mecánica de la conmutación es hacer-y-rompe el material del contacto del AG -- la aleación Ni-basada con las partículas del metal del Ni dispersadas en esto que se obtiene con mezclar y el revolvimiento de 3.1 a 20.0 pesos % de polvo del Ni, de cierta cantidad de polvo de Li.sub.2 CO.sub.3 que corresponde a 0.01 a 0.50 peso % de li del metal como añadido, y de un equilibrio que es polvo del AG para hacer una mezcla con los polvos arriba descritos dispersados uniformemente en esto, y con la condensación y la sinterización de la mezcla arriba descrita.