A method of making a small-diameter through hole having high reliability
with regard to a hole wall at a high rate with the energy of a high-output
carbon dioxide gas laser without pre-making any hole in a copper foil,
forming or disposing a coating or a sheet of an organic substance
containing 3 to 97% by volume of at least one powder selected from the
group consisting of a metal compound powder, a carbon powder and metal
powder which have a melting point of at least 900.degree. C. and a bond
energy of at least 300 KJ/mol on at least a copper foil surface to be
irradiated with the carbon dioxide gas laser, and irradiating a surface
thereof with necessary pulses of the carbon dioxide gas laser to form the
penetration hole, and an auxiliary material for use when a penetration
hole is made in the copper-clad laminate with a carbon dioxide gas laser,
the auxiliary material being a coating or a sheet of an organic substance
containing 3 to 97% by volume of at least one powder selected from the
group consisting of a metal compound powder, a carbon powder and metal
powder which have a melting point of at least 900.degree. C. and a bond
energy of at least 300 KJ/mol.
Een methode van een makende klein-diameter door gat dat hoge betrouwbaarheid met betrekking tot een gatenmuur heeft aan een hoog tarief met de energie van een high-output laser van het kooldioxidegas zonder pre-maakt enig gat in een koperfolie, het vormen van of een deklaag of een blad van een organische substantie te schikken die 3 tot 97% in volume van minstens één poeder dat uit de groep wordt geselecteerd bevat die uit een poeder van de metaalsamenstelling bestaat, een koolstofpoeder en metaalpoeder die een smeltpunt van minstens 900.degree. C. en een bandenergie van minstens 300 kJ/mol op minstens een oppervlakte van de koperfolie dat met de laser van het kooldioxidegas moet worden bestraald, en het bestralen a hebben gh rate with the energy of a high-output carbon dioxide gas laser without pre-making any hole in a copper foil, forming or disposing a coating or a sheet of an organic substance containing 3 to 97% by volume of at least one powder selected from the group consisting of a metal compound powder, a carbon powder and metal powder which have a melting point of at least 900.degree. C. and a bond energy of at least 300 KJ/mol on at least a copper foil surface to be irradiated with the carbon dioxide gas laser, and irradiating a surface thereof with necessary impulsen van de laser van het kooldioxidegas om het penetratiegat te vormen, en een hulpmateriaal voor gebruik wanneer een penetratiegat in het koper-beklede laminaat met een laser van het kooldioxidegas wordt gemaakt, het hulp materiaal dat een deklaag of een blad van een organische substantie die 3 tot 97% in volume van minstens één poeder dat uit de groep wordt geselecteerd is bevat die uit een poeder van de metaalsamenstelling bestaat, een koolstofpoeder en metaalpoeder die een smeltpunt van minstens 900.degree. C. en een bandenergie van minstens 300 kJ/mol hebben.