The present invention is envisioned to improve sliding characteristics of
polyether aromatic ketone resins and to provide their molded articles
which are themselves resistant to damage and abrasion, cause no such
damage or abrasion to their partner parts and can be easily molded. Thus,
the present invention pertains to a polyether aromatic ketone resin
composition comprising a polyether aromatic ketone resin and a
high-hardness filler having a Mohs hardness of 6 or higher, the content of
said filler being 1 to 100 parts by weight per 100 parts by weight of said
ketone resin, and furthermore to a film or sheet made of the resin
composition. The high-hardness filler having a Mohs hardness of 6 or
higher is preferably particulate or spherical in particle shape. Also, the
maximal particle size of said high-hardness filler is preferably not
larger than 100 .mu.m.
La presente invenzione è prevista per migliorare fare scorrere le caratteristiche delle resine aromatiche del chetone del polietere e per fornire i loro articoli modellati che sono essi stessi resistenti a danni e ad abrasione, non causa tale danneggiamento o abrasione delle loro parti del socio e può essere modellata facilmente. Quindi, la presente invenzione appartiene una composizione aromatica nella resina del chetone del polietere che contiene una resina aromatica del chetone del polietere e un riempitore di alto-durezza che hanno una durezza di Mohs di 6 o più alto, il contenuto del riempitore detto che è 1 - 100 parti di peso per 100 parti del peso della resina detta del chetone ed ancora ad una pellicola o ad un foglio fatto della composizione della resina. Il riempitore di alto-durezza che ha una durezza di Mohs di 6 o l'più alto è preferibilmente polverizzato o sferico nella figura della particella. Inoltre, la dimensione delle particelle massima del riempitore detto di alto-durezza non è preferibilmente più grande di il mu.m 100.