The invention relates to a process for preparing electrically conductive
pigments based on F.sup.- - and/or PO.sub.4.sup.3- -doped tin mixed oxides
applied as an electrically conductive layer to a substrate, in which,
first of all, SnO.sub.2 -coated substrates are prepared by precipitation
and subsequent calcining and then, in further process steps, this
SnO.sub.2 layer is converted into a tin mixed oxide layer doped with
F.sup.- and/or PO.sub.4.sup.3-. The invention further relates to
electrically conductive pigments prepared by the process of the invention,
to the use of these pigments for pigmenting lacquers, printing inks,
plastics systems or coatings, and to lacquers, printing inks, plastics
systems or coatings pigmented with an electrically conductive pigment
prepared by the process of the invention.
De uitvinding heeft op een proces om geleidend pigment betrekking elektrisch voor te bereiden dat op F.sup wordt gebaseerd. - - en/of worden PO.sub.4.sup.3- - gesmeerde tin gemengde oxyden die als elektrisch geleidende laag op een substraat worden toegepast, waarin, eerst en vooral, SnO.sub.2 - met een laag bedekte substraten voorbereid door precipitatie en het verdere calcineren en toen, in verdere processtappen, deze laag SnO.sub.2 worden in een tin gemengde oxydelaag omgezet die met F.sup. wordt gesmeerd - en/of PO.sub.4.sup.3 -. De uitvinding heeft verder op elektrisch geleidend pigment dat door het proces van de uitvinding wordt voorbereid, op het gebruik van dit pigment voor het met pigment kleuren van lak, drukinkten, plastiekensystemen of deklagen, en op lak, drukinkten, plastiekensystemen of deklagen betrekking die met een elektrisch geleidend pigment met pigment worden gekleurd dat door wordt voorbereid