The present invention provides a polymer alloy including from about 40% to
about 75% by weight of at least one polyamide, from about 10% to about 50%
by weight polypropylene, from about 0.01% to about 1.0% by weight of at
least one block copolymer including a vinyl aromatic monomer and a
conjugated diene, and also includes an unsaturated dicarboxylic reagent,
from about 0.1% to about 5.0% by weight of at least one block copolymer or
terpolymer, wherein the terpolymer may have an unsaturated dicarboxylic
reagent grafted thereto, from about 0.01% to about 7.5% of a
compatibilizing agent, and from about 5% to about 50% by weight of a
filler. The alloy of the present invention exhibits improved knitline
strength and improved drop impact results compared with prior art
fiberglass-reinforced nylon blends.
Die anwesende Erfindung stellt eine Polymer-Plastik Legierung zur Verfügung, die von ungefähr 40% bis ungefähr 75% nach Gewicht von mindestens einem Polyamid, von ungefähr 10% bis ungefähr 50% nach Gewicht Polypropylen, von ungefähr 0.01% bis ungefähr 1.0% nach Gewicht von mindestens einem Blockcopolymer einschließlich eine Vinylaromatische Monomere und ein konjugiertes Dien einschließt und schließt auch ein ungesättigtes dicarbonisches Reagens, von ungefähr 0.1% bis ungefähr 5.0% nach Gewicht von mindestens einem Blockcopolymer oder -terpolymer, worin das Terpolymer ein ungesättigtes dicarbonisches Reagens haben mit ein kann, das dazu verpflanzt wird, von ungefähr 0.01% bis ungefähr 7.5% eines compatibilizing Mittels und von ungefähr 5% bis ungefähr 50% nach Gewicht eines Füllers. Die Legierung der anwesenden Erfindung stellt verbesserte knitline Stärke aus und die verbesserten Tropfenauswirkung Resultate, die mit Fiberglas-verstärktem Nylon der vorherigen kunst verglichen werden, mischt.