Clinkered materials containing high concentrations of {(C,K,N,M).sub.4
(A,F,Mn,P,T,S).sub.3 Cl,S)}(crystal X), and {C.sub.2 S).sub.3 (CS).sub.3
Ca(f,Cl).sub.2 } or C.sub.9 S.sub.3 S.sub.3 Ca(f,cl).sub.2 crystal Y),
and/or {C.sub.5 S.sub.2 S) (crystal Z) directly from the kiln, rapidly
hardening ultra-high early strength cement including these clinkered
materials, methods for forming and using said compositions and the cements
so produced are claimed. The methods include the steps of forming a
mixture of raw material containing CaO, MgO, Al.sub.2 O.sub.3, Fe.sub.2
O.sub.3, TiO.sub.2, Mn.sub.2 O.sub.5, SiO.sub.2, SO.sub.3, Na.sub.2 O,
K.sub.2 O, P.sub.2 O.sub.5 and F, respectively designated C, M, A, F, T,
Mn, S, S, N, K, P and f, and heating said mixture to an elevated
temperature between 900.degree. C. and 1,200.degree. C.; before
determining average amount of crystals X, Y, and Z. Final mixtures
comprising these clinkers and hydraulic or portland type cement are made
to produce cement compositions having crystal X concentrations of
approximately 5% to 35% by weight, crystal Y concentrations of
approximately 5% to 40% by weight, and/or crystal Z concentrations of
approximately 5% to 40% by weight, with the remainder being hydraulic or
portland type cement. The cements so produced are rapid hardening and
exhibit high strengths ranging from 2,000 psi to 7,000 psi in one hour,
6,000 to 8,000 psi in one day and 9,000 to 12,000 psi in 28 days. They are
sulfate and sea-water attack resistant and have low heats of hydration,
minimal shrinkage, and high water impermeability. The methods claimed also
results in significant reduction in gaseous emissions including SO.sub.x,
NO.sub.x and CO.sub.x.
Materiali di Clinkered che contengono le alte concentrazioni di {(C, K, N, M).sub.4 (A, F, manganese, P, T, S).sub.3 Cl, S)}(crystal X) e {C.sub.2 S).sub.3 (CS).sub.3 Ca(f, Cl).sub.2} o C.sub.9 S.sub.3 S.sub.3 Ca(f, cl).sub.2 cristallo Y) e/o {C.sub.5 S.sub.2 S) (cristallo Z) direttamente dal forno, indurente velocemente il cemento in anticipo ultraelevato di resistenza compreso questi clinkered i materiali, metodi per formare ed usando le composizioni dette ed i cementi in modo da prodotto sono esatti. I metodi includono i punti di formare una miscela di materia prima che contiene il cao, il MgO, Al.sub.2 O.sub.3, Fe.sub.2 O.sub.3, TiO.sub.2, Mn.sub.2 O.sub.5, SiO.sub.2, SO.sub.3, Na.sub.2 O, K.sub.2 O, P.sub.2 O.sub.5 e F, rispettivamente indicata C, m., A, F, T, manganese, S, S, N, K, P e f e riscaldante la miscela detta ad una temperatura elevata fra 900.degree. C. e 1,200.degree. C.; prima della determinazione della quantità media di cristalli X, Y e le miscele dello Z. Final che contengono questi clinkers ed il tipo cemento de Portland o idraulico sono fatti per produrre le composizioni nel cemento che hanno le concentrazioni di cristallo in X di circa 5% - 35% di peso, le concentrazioni di cristallo in Y di circa 5% - 40% di peso e/o concentrazioni di cristallo in Z di circa 5% - 40% di peso, con il resto che è tipo cemento de Portland o idraulico. I cementi in modo da prodotto sono indurimento veloce ed esibiscono le alte resistenze che variano da 2.000 PSI a 7.000 PSI in un'ora, 6.000 - 8.000 PSI in un giorno e 9.000 - 12.000 PSI in 28 giorni. Sono attacco dell'acqua di mare e del solfato resistente ed hanno livello basso riscaldano di idratazione, del restringimento minimo e di alta impermeabilità dell'acqua. I metodi hanno esatto inoltre i risultati nella riduzione significativa delle emissioni gassose compreso SO.sub.x, NO.sub.x e CO.sub.x.