A process is described for treating molten metal with a particulate
treating agent. A melt of a metal, e.g. aluminum, is provided in a
treatment vessel such as a ladle and a mixing impeller is positioned
substantially below the surface of the molten metal. The impeller
comprises a plate with a series of spaced blades extending from the
surface of the plate. This impeller is adapted to provide high shear
mixing with minimum vortex. While rotating the impeller on a substantially
vertical axis, particulate treating agent is fed by way of an injection
tube below the surface of the molten metal and into the region between the
axis and periphery of the impeller. This causes a high shearing action in
the region of the blades whereby the treating agent is quickly broken down
into finely divided droplets that are at least partially molten and which
are circulated within the molten metal.
Μια διαδικασία περιγράφεται για τη μεταχείρηση του λειωμένου μετάλλου με έναν μοριακό μεταχειριμένος πράκτορα. Ένα λειωμένο μέταλλο ενός μετάλλου, π.χ. αργίλιο, παρέχεται σε ένα σκάφος επεξεργασίας όπως μια κουτάλα και ένα αναμιγνύοντας στροφείο τοποθετείται ουσιαστικά κάτω από την επιφάνεια του λειωμένου μετάλλου. Το στροφείο περιλαμβάνει ένα πιάτο με μια σειρά χωρισμένων κατά διαστήματα λεπίδων που επεκτείνεται από την επιφάνεια του πιάτου. Αυτό το στροφείο προσαρμόζεται για να παρέχει την υψηλή κουρά αναμιγνύοντας με την ελάχιστη δίνη. Περιστρεφόμενος το στροφείο σε έναν ουσιαστικά κάθετο άξονα, ο μοριακός μεταχειριμένος πράκτορας ταϊ'ζεται μέσω ενός σωλήνα εγχύσεων κάτω από την επιφάνεια του λειωμένου μετάλλου και στην περιοχή μεταξύ του άξονα και της περιφέρειας του στροφείου. Αυτό προκαλεί μια υψηλή δράση κουράς στην περιοχή των λεπίδων με το οποίο ο μεταχειριμένος πράκτορας χωρίζεται γρήγορα σε λεπτά διαιρεμένα σταγονίδια που είναι τουλάχιστον μερικώς λειωμένα και που κυκλοφορούν μέσα στο λειωμένο μέταλλο.