Silicone material crosslinkable into silicone elastomer by polyaddition
reactions is described. A material is provided offering a compromise
between the following characteristics: fluidity (in non-crosslinked
state), hydrophilicity (in non-crosslinked or crossliked state) and high
mechanical properties (in crosslinked state). The following materials are
added to crosslinkable silicone material: (i) a reinforcing siliceous
filler in the form of a suspension obtained by subjecting the filler to a
treatment in two stages by an agent providing compatibility and by
operating in the presence of a polyorganosiloxane with Si-alkenyl
functions; and (ii) one or more non-ionic, ionic or amphoteric
surfactants. Said silicone material is particularly useful for
impressions, for example dental impressions and for making pads used in
pad printing techniques.
Materiële wordt crosslinkable van het silicone in siliconeelastomeer door polyadditionreacties beschreven. Een materiaal wordt verstrekt aanbiedend een compromis tussen de volgende kenmerken: vloeibaarheid (in niet-crosslinked staat), hydrophilicity (in niet-crosslinked of crossliked staat) en hoge mechanische eigenschappen (in crosslinked staat). De volgende materialen worden toegevoegd aan crosslinkable siliconemateriaal: (i) een versterkende kiezelvuller in de vorm van een opschorting die door de vuller aan een behandeling in twee stadia te onderwerpen door een agent die verenigbaarheid voorziet en door in aanwezigheid van een polyorganosiloxane wordt verkregen te werken van Si-Si-alkenyl functies; en (ii) één of meerdere niet-ionische, Ionische of amfotere capillair-actieve stoffen. Het bovengenoemde siliconemateriaal is bijzonder nuttig voor indrukken, bijvoorbeeld tandindrukken en voor het maken van stootkussens die in de technieken van de stootkussendruk worden gebruikt.