This invention relates to high performance RIM (reaction injection molded)
poly(urethane)urea elastomers, and to a process for their production.
These elastomers comprise the reaction product of an allophanate-modified
diphenylmethane diisocyanate prepolymer having an NCO group content of
about 5 to about 30%, with an isocyanate-reactive component comprising a
high molecular weight amine-terminated polyether polyol, an aromatic
diamine chain extender, and, optionally, a chain extender or crosslinker
selected from the group consisting of aliphatic amine terminated polyether
polyols and aliphatic hydroxyl terminated polyether polyols, optionally,
in the presence of an internal mold release agent, a surfactant and a
filler.
Этот вымысел относит к эластомерам poly(urethane)urea ОПРАВЫ высокого класса исполнения (отлитой в форму впрыски реакции), и к процессу для их продукции. Эти эластомеры состоят из продукта реакции аллопюанате-dorabotannogo преполимера diisocyanate diphenylmethane имея содержание группы nco около 5 до около 30%, при изоцианат-reaktivny1 компонент состоя из амин-prekra5ennogo high molecular weight полиола polyether, ароматичного разбивателя цепи диамина, и, опционно, цепных разбивателя или crosslinker выбранных от группы consist of алифатическим прекращенные амином полиолы polyether и алифатическим прекращенные гидроксилом полиолы polyether, опционно, in the presence of внутренне вещество отпуска прессформы, сурфактант и заполнитель.