A method of manufacturing a high Mn non-magnetic steel sheet having low
permeability at a cryogenic temperature suitable for use in large scale
particle accelerators, the method comprises rolling a steel material
containing, on the wt % basis, from 0.05 to 0.18% of C, from 26.0 to 30.0%
of Mn, from 5.0 to 10.0% of Cr, 0.05 to 0.15% of N and, optionally, from
0.50 to 5.0% of Ni, in which a rolling start temperature is from 1050 to
1200.degree. C. and a rolling end temperature is from 700 to 1000.degree.
C. Further, a cold rolled sheet is annealed at an annealing temperature
for cold rolled sheet of from 1050 to 1200.degree. C. and cooled after
annealing, the annealed sheet being preferably applied with temper rolling
under control for the strength by varying a draft ratio.
Μια μέθοδος ένα υψηλό φύλλο χάλυβα ΜΝ non-magnetic που έχει τη χαμηλή διαπερατότητα σε μια κρυογόνο θερμοκρασία κατάλληλη για τη χρήση στους επιταχυντές μορίων μεγάλης κλίμακας, η μέθοδος περιλαμβάνει το κύλισμα ενός υλικού χάλυβα που περιέχει, στη wt% βάση, από 0,05 σε 0,18% του γ, από 26,0 σε 30,0% του ΜΝ, από 5,0 σε 10,0% του χρωμίου, 0,05 0,15% του ν και, προαιρετικά, από 0,50 σε 5,0% του Νι, στο οποίο μια θερμοκρασία έναρξης κυλίσματος είναι από 1050 σε 1200.degree. Γ. και μια θερμοκρασία τελών κυλίσματος είναι από 700 σε 1000.degree. Γ. Περαιτέρω, ένα φύλλο ψυχρής έλασης ανοπτείται σε μια ανοπτώντας θερμοκρασία για το φύλλο ψυχρής έλασης από 1050 σε 1200.degree. Γ. και δροσίζεται μετά από να ανοπτήσει, το ανοπτημένο φύλλο κατά προτίμηση που εφαρμόζεται με την ιδιοσυγκρασία που κυλά υπό έλεγχο για τη δύναμη με την ποικιλία μιας αναλογίας σχεδίων.