Metal oxides having a perovskite or perovskite-like crystal structure are
prepared by a process comprising subjecting a mixture of starring powders
to a high energy milling sufficient to induce chemical reaction of the
components and thereby directly mechanosynthesize said metal oxide in the
form of a perovskite or a perovskite-like material having a
nanocrystalline structure as determined by X-ray diffractometry. The
process according to the present invention is simple, efficient, not
expensive and does not require any heating step for producing a perovskite
that may easily show a very high specific surface area. Another advantage
is that the perovskite obtained according to the present invention also
has a high density of lattice defects thereby showing a higher catalytic
activity, a characteristic which is highly desirable in their eventual
application as catalysts and electronic conductors.
Τα μεταλλικά οξείδια που έχουν perovskite ή περοβσκητε-όπως μια δομή κρυστάλλου προετοιμάζονται με μια διαδικασία περιλαμβάνοντας υποβάλλοντας ένα μίγμα με πρωταγωνιστή σκονών σε μια υψηλή ενεργειακή άλεση επαρκή για να προκαλέσει τη χημική αντίδραση των συστατικών και με αυτόν τον τρόπο άμεσα το εν λόγω μεταλλικό οξείδιο υπό μορφή perovskite ή περοβσκητε-όπως υλικού που έχει μια δομή nanocrystalline όπως καθορίζονται από των ακτίνων X diffractometry. Η διαδικασία σύμφωνα με την παρούσα εφεύρεση είναι απλή, αποδοτική, μη ακριβή και δεν απαιτεί οποιοδήποτε βήμα θέρμανσης για την παραγωγή perovskite που μπορεί εύκολα να παρουσιάσει πολύ υψηλή συγκεκριμένη περιοχή επιφάνειας. Ένα άλλο πλεονέκτημα είναι ότι perovskite που λαμβάνεται σύμφωνα με την παρούσα εφεύρεση έχει επίσης μια υψηλή πυκνότητα των ατελειών δικτυωτού πλέγματος με αυτόν τον τρόπο που παρουσιάζουν υψηλότερη καταλυτική δραστηριότητα, ένα χαρακτηριστικό που είναι ιδιαίτερα επιθυμητό στην ενδεχόμενη αίτησή τους ως καταλύτες και ηλεκτρονικούς αγωγούς.