The present invention is directed to the method of extruding a
thermoplastic co-polyester EMA (ethyl methyl acrylate) blended film at
temperatures well above the melt temperature of the base thermoplastic
co-polyester, the co-polyester/EMA film having enhanced barrier
properties. Notably, the present invention contemplates extrusion of
co-polyester compounds onto suitable substrates without the need to employ
antioxidant compounds in the molten polymer material. A further aspect of
the present invention entails a film comprising an EMA and co-polyester
thermoplastic admixed with a compatibilizer and extruded at a temperature
at least 10% higher than the melt temperature, which in turn provides the
co-polyester film with durable adhesive properties in addition to good
breathability as measured by moisture vapor transmission rate (MVTR).
De onderhavige uitvinding wordt geleid aan de methode om een thermoplastische mede-polyesterema (ethyl methylacrylate) gemengde film goed uit te drijven bij temperaturen boven de smeltingstemperatuur van de basis thermoplastische mede-polyester die, de mede-polyester/EMA film barrièreeigenschappen heeft verbeterd. In het bijzonder, de onderhavige uitvinding uitdrijving van mede-polyestersamenstellingen op geschikte substraten zonder de behoefte overweegt om anti-oxyderende samenstellingen in het gesmolten polymeermateriaal aan te wenden. Een verder aspect van de onderhavige uitvinding brengt een film met zich mee bestaand uit thermoplastische EMA en een mede-polyester vermengd met een compatibilizer en uitgedreven bij een temperatuur minstens 10% hoger dan de smeltingstemperatuur, die beurtelings de mede-polyesterfilm van duurzame zelfklevende eigenschappen naast goede breathability zoals die door de transmissietarief wordt gemeten voorziet van de vochtigheidsdamp (MVTR).