A process for depositing metal on microparticulate comprising immersing
microparticulate in an autocatalytic plating bath comprising the metal;
inducing ultrasonic vibration in the plating bath at a frequency
corresponding to resonance frequency of the microparticulate; and inducing
a turbulent vibration signal in the plating bath in a direction
non-parallel to the ultrasonic vibration. This process results in the
autocatalytic plating bath depositing the metal on the microparticulate
with uniform thickness. The microparticulate can be spheres, flakes or
microfibers, and can be made from a number of materials, such as synthetic
polymers (nylon, Kevlar.TM., Zylon.TM., and aramid fibers) and
biodegradable compounds. A method is disclosed for coating a surface with
metallized microparticulate fibers with an orientation perpendicular to
the surface.
Un procédé pour déposer le métal sur le microparticulate comportant immergeant le microparticulate dans un bain autocatalytique d'électrodéposition comportant le métal ; induire la vibration ultrasonique dans le bain d'électrodéposition à une fréquence correspondant à la fréquence de résonance du microparticulate ; et induisant un signal turbulent de vibration dans le bain d'électrodéposition dans une direction non-parallèle à la vibration ultrasonique. Ce processus a comme conséquence le bain autocatalytique d'électrodéposition déposant le métal sur le microparticulate avec l'épaisseur uniforme. Le microparticulate peut être des sphères, des flocons ou des microfibers, et peut être fait à partir d'un certain nombre de matériaux, tels que les polymères synthétiques (nylon, Kevlar.TM., Zylon.TM., et fibres d'aramid) et les composés biodégradables. Une méthode est révélée pour enduire une surface des fibres métallisées de microparticulate avec une perpendiculaire d'orientation sur la surface.