Particulate materials are cold molded by preheating a binder and the
material to be bound to a temperature of from 160 to 240.degree. C., and
then press molding at a temperature less than 80.degree. C. and at a
pressure of from 1 to 120 bar to give a molding, wherein the binder
contains a polymer powder or aqueous polymer dispersion thereof, the
polymer having a glass transition temperature Tg greater than 80.degree.
C. and a complex viscosity less than 15,000 Pa.multidot.s at 190.degree.
C., and derived from one or more comonomer units from the group of vinyl
esters of optionally branched C.sub.1-18 alkylcarboxylic acids,
(meth)acrylic esters of optionally branched C.sub.1-15 alcohols, dienes,
olefins, vinylaromatics, and vinyl halides. The moldings exhibit excellent
properties including resistance to sagging at elevated temperatures, and
are recyclable.
Les matériaux particulaires sont froid moulé en préchauffant une reliure et le matériel à lier à une température de de 160 à 240.degree. Le C., et serrent alors le bâti à une température moins que 80.degree. C. et à une pression de barre de 1 à 120 pour donner un bâti, où la reliure contient une poudre de polymère ou dispersion aqueuse de polymère en, le polymère ayant une température de transition de verre Tg 80.degree plus grand que. C. et une viscosité complexe moins de 15.000 Pa.multidot.s à 190.degree. C., et dérivé à partir d'une ou plusieurs unités de comonomère du groupe d'esters de vinyle des acides C.sub.1-18 alkylcarboxylic sur option embranchés, (esters meth)acrylic d'alcools C.sub.1-15, de diènes, d'oléfines, de vinylaromatics, et d'halogénures sur option embranchés de vinyle. Les bâtis présentent d'excellentes propriétés comprenant la résistance au fléchissement aux températures élevées, et sont recyclables.