One method of the present invention relates to a method for spray forming
metal deposits. The method is comprised of providing a ceramic substrate
having a spraying pattern for receiving sprayed metal particles, spraying
metal particles onto the spraying pattern to form a metal deposit on the
spraying pattern for at least a first spray period, controlling the
spraying step during the first spray period so that the temperature of the
deposited metal particles increases at an average rate of less than or
equal to about 15.degree. per minute. The first spray period can be
defined as lasting until the temperature of the deposited metal particles
is at or about a steady state temperature. The steady state temperature is
preferably in the range of about 330.degree. C. to about 370.degree. C.
Μια μέθοδος της παρούσας εφεύρεσης αφορά μια μέθοδο για τον ψεκασμό που διαμορφώνει τις καταθέσεις μετάλλων. Η μέθοδος αποτελείται από την παροχή ενός κεραμικού υποστρώματος που έχει ένα ψεκάζοντας σχέδιο για τη λήψη των ψεκασμένων μορίων μετάλλων, ψεκασμός των μορίων μετάλλων επάνω στο ψεκάζοντας σχέδιο για να διαμορφώσει μια κατάθεση μετάλλων στο ψεκάζοντας σχέδιο για τουλάχιστον μια πρώτη περίοδο ψεκασμού, που ελέγχει το ψεκάζοντας βήμα κατά τη διάρκεια της πρώτης περιόδου ψεκασμού έτσι ώστε η θερμοκρασία των κατατεθειμένων μορίων μετάλλων αυξάνεται σε ένα μέσο ποσοστό λιγότερο ή ίσο προς για του 15.degree. ανά λεπτό. Η πρώτη περίοδος ψεκασμού μπορεί να οριστεί ως μόνιμη έως ότου είναι η θερμοκρασία των κατατεθειμένων μορίων μετάλλων σε ή για μια θερμοκρασία σταθερού κράτους. Η θερμοκρασία σταθερού κράτους είναι κατά προτίμηση περίπου 330.degree. Γ. σε περίπου 370.degree. γ.