The invention relates to adhesives manufacturing. These adhesives are used
in household and industry for adhering various materials (concrete,
ceramics, different coatings, etc) exploited under temperatures
+50.degree. C. to -20.degree. C and under elevated humidity. The adhesive
composition represents the product of interaction between potassium
silicate aqueous solution (density of 1.3 to 1.37 g/cm.sup.3, molar ratio
SiO.sub.2 /K.sub.2 O of 3.4 to 3.7), anhydrous lithium hydroxide mixed
with di- or trihydric alcohol, vollastonite (particle size of 150 .mu.m
and smaller, length to diameter ratio 5-3:1), talc (particle size of 10 to
20 .mu.m mainly) and inorganic pigment. The adhesive composition is
prepared by a given consecutive mixture of components. The adhesive
composition has enhanced activity (storage stability) and water
resistance. It also has improved strength of adhesion junction while
adhering various materials; it is non-toxic and pollution-free.
A invenção relaciona-se a manufaturar dos adesivos. Estes adesivos são usados na casa e na indústria aderindo os vários materiais (concreto, ceramics, revestimentos diferentes, etc.) explorados sob temperaturas +50.degree. C. a -20.degree. C e sob a umidade elevated. A composição adesiva representa o produto da interação entre a solução aqueous do silicato do potassium (densidade de 1.3 a 1.37 g/cm.sup.3, relação molar SiO.sub.2 /K.sub.2 O de 3.4 a 3.7), o hydroxide anhydrous do lítio misturado com o álcool di- ou trihydric, o vollastonite (tamanho de partícula do mu.m 150 e menor, o comprimento à relação 5-3:1 do diâmetro), talc (tamanho de partícula do mu.m 10 a 20 principalmente) e pigment inorgánico. A composição adesiva é preparada por uma mistura consecutiva dada dos componentes. A composição adesiva realçou a atividade (estabilidade do armazenamento) e a resistência de água. Também melhorou a força da junção da adesão ao aderir vários materiais; é non-toxic e poluição-livre.