The present invention provides a raw material composition for soda-lime
glass capable of effectively suppressing formation of nickel sulfide (NiS)
in the course of melting of the glass raw material. A nickel sulfide (NiS)
impurity present in soda-lime glass is formed in a high-temperature
vitrification step in which metal particles containing Ni and an Ni
component of stainless steel used for the interior of a melting furnace,
which are mixed into glass raw material, react at high temperature with a
sulfur (S) component in Na.sub.2 SO.sub.4 serving as a glass raw material.
However, when an additive containing an oxide, a chloride, a sulfate, or a
nitrate of a metal is added in a very small amount and in advance to glass
raw material, formation of NiS by the reaction between Ni and S in the
course of melting can be suppressed or completely eliminated.
Η παρούσα εφεύρεση παρέχει μια σύνθεση πρώτης ύλης για το soda-lime γυαλί ικανό αποτελεσματικά το σχηματισμό του σουλφιδίου νικελίου (NiS) κατά τη διάρκεια της τήξης της πρώτης ύλης γυαλιού. Μια ακαθαρσία σουλφιδίου νικελίου (NiS) παρούσα στο soda-lime γυαλί διαμορφώνεται σε ένα υψηλής θερμοκρασίας βήμα υαλοποίησης στο οποίο τα μόρια μετάλλων που περιέχουν το Νι και ένα τμήμα Νι του ανοξείδωτου χάλυβα χρησιμοποίησαν για το εσωτερικό ενός λειώνοντας φούρνου, τα οποία αναμιγνύονται στο γυαλί που η πρώτη ύλη, αντιδρά στην υψηλή θερμοκρασία με ένα τμήμα θείου (S) σε Na.sub.2 SO.sub.4 που χρησιμεύει ως μια πρώτη ύλη γυαλιού. Εντούτοις, όταν προστίθεται μια πρόσθετη ουσία που περιέχει ένα οξείδιο, ένα χλωρίδιο, ένα θειικό άλας, ή ένα νιτρικό άλας ενός μετάλλου σε ένα πολύ μικρό ποσό και εκ των προτέρων στην πρώτη ύλη γυαλιού, ο σχηματισμός NiS από την αντίδραση μεταξύ του Νι και του s κατά τη διάρκεια της τήξης μπορεί να κατασταλθεί ή να αποβληθεί πλήρως.