A pigment having weak dispersion force to be readily dispersed in a medium
to be colored from which an excellent yellow image having superior
transparency can be produced. The pigment includes a compound having the
same chemical formula as C.I. Pigment Yellow 180. The BET specific surface
area based on the nitrogen absorption process of the pigment is 20-100
m.sup.2 /g, and the ratio of the absolute strength of X-ray diffraction at
Bragg angle 2.theta.=17.5.degree..+-.0.2.degree. to the absolute strength
of X-ray diffraction at Bragg angle 2.theta.=18.2.degree..+-.0.2.degree.
of the pigment in a powder X-ray diffraction diagram using a CuK.alpha.
characteristic X-ray is less than 1.8/1.0. The present invention also
provides a dispersion including the pigment and a thermoplastic resin
having excellent transparency and color strength.
Μια χρωστική ουσία που έχει την αδύνατη δύναμη διασποράς που διασκορπίζεται εύκολα σε ένα μέσο που χρωματίζεται από το οποίο μια άριστη κίτρινη εικόνα που έχει την ανώτερη διαφάνεια μπορεί να παραχθεί. Η χρωστική ουσία περιλαμβάνει μια ένωση που έχει τον ίδιο χημικό τύπο με C.I. τη χρωστική ουσία κίτρινα 180. Η συγκεκριμένη περιοχή επιφάνειας ΣΤΟΙΧΗΜΑΤΟΣ βασισμένη στη διαδικασία απορρόφησης αζώτου της χρωστικής ουσίας είναι 20-100 m.sup.2/g, και η αναλογία της απόλυτης δύναμης της των ακτίνων X διάθλασης Bragg στη γωνία 2.theta.=17.5.degree..+-.0.2.degree. στην απόλυτη δύναμη της των ακτίνων X διάθλασης Bragg στη γωνία 2.theta.=18.2.degree..+-.0.2.degree. από τη χρωστική ουσία σε ένα των ακτίνων X διάγραμμα διάθλασης σκονών που χρησιμοποιεί ένα CuK.alpha. η χαρακτηριστική ακτίνα X είναι λιγότερο από 1.8/1.0. Η παρούσα εφεύρεση παρέχει επίσης μια διασπορά συμπεριλαμβανομένης της χρωστικής ουσίας και μιας θερμοπλαστικής ρητίνης που έχουν την άριστη δύναμη διαφάνειας και χρώματος.