This specification describes an optical polycarbonate composition obtained
by the melt polycondensation of a bisphenol and a carbonic diester in the
presence of an alkaline compound catalyst, wherein said optical
polycarbonate composition comprises (i) a compound expressed by the
following Formula [A] in an amount of 30 to 2000 ppm; (ii) a compound
expressed by the following Formula [B] in an amount of 30 to 4000 ppm; and
(iii) a compound expressed by the following Formula [C] in an amount of 80
to 8000 ppm. The polycarbonate composition has a viscosity average
molecular weight of between 12,000 and 18,000, and the portion with a
molecular weight (as measured by GPC) of 1000 or less accounts for 0.5 to
1.5 wt %.
##STR1##
Αυτή η προδιαγραφή περιγράφει μια οπτική σύνθεση πολυανθράκων που λαμβάνεται από την πολυσυμπύκνωση λειωμένων μετάλλων ενός bisphenol και ενός ανθρακικού διεστέρα παρουσία ενός αλκαλικού σύνθετου καταλύτη, όπου η εν λόγω οπτική σύνθεση πολυανθράκων περιλαμβάνει (ι) μια ένωση που εκφράζεται από τον ακόλουθο τύπο [ Α ] σε ένα ποσό 30 έως 2000 PPM (II) μια ένωση που εκφράζεται από τον ακόλουθο τύπο [ β ] σε ένα ποσό 30 έως 4000 PPM και (III) μια ένωση που εκφράζεται από τον ακόλουθο τύπο [ γ ] σε ένα ποσό 80 έως 8000 PPM. Η σύνθεση πολυανθράκων έχει ένα μέσο μοριακό βάρος ιξώδους μεταξύ 12.000 και 18.000, και τη μερίδα με ένα μοριακό βάρος (όπως μετριέται από GPC) 1000 ή λιγότερων απολογισμών για 0,5 έως 1,5 βάρος %. ## STR1 ##