The invention relates to porous fiber comprising a polymeric material, said
fiber having a diameter of 20 to 4000 nm and pores in the form of channels
extending at least to the core of said fiber and/or through said fiber.
The process for producing the porous fiber comprises electrospinning a 5 to
20% by weight solution of at least one polymer in an organic solvent using
an electric field above 10.sup.5 V/m to obtain a fiber having a diameter
of 20 to 4000 nm and pores in the form of channels extending at least to
the core of said fiber and/or through said fiber.
The porous fiber may be used as a carrier for a catalyst, as an adsorbent
or absorbent or as a biomaterial, may be chemically modified or
functionalized or may be used as a template for producing highly porous
solids.
La invención se relaciona con la fibra porosa que abarca un material polimérico, fibra dicha que tiene un diámetro de 20 a 4000 nm y poros en la forma de canales que extienden por lo menos a la base de la fibra dicha y/o a través de la fibra dicha. El proceso para producir la fibra porosa abarca electrospinning 5 a el 20% al lado de la solución del peso por lo menos de un polímero en un solvente orgánico usando un campo eléctrico sobre 10.sup.5 V/m para obtener una fibra que tiene un diámetro de 20 a 4000 nm y poros en la forma de canales que extienden por lo menos a la base de la fibra dicha y/o a través de la fibra dicha. La fibra porosa se puede utilizar como portador para un catalizador, como un adsorbente o absorbente o como biomaterial, se puede químicamente modificar o functionalized o se puede utilizar como plantilla para producir los sólidos altamente porosos.