A compound is provided having the means of intumescence at temperatures
above 195.degree. C. to 220.degree. C.
The compound is an intumescent powder defined by the molar ratios (2.20 to
3.70) SiO.sub.2 /(0.20 to 0.35) Li.sub.2 O: (0.65 to 0.80)(Na.sub.2
O+K.sub.2 O) where the coefficients of Li.sub.2 O and of (Na.sub.2
O+K.sub.2 O) total 1.00 and thermoplastic material having a plastic state
at less than 195.degree. C. If the thermoplastic contains a halogen, as
does Polyvinyl Chloride (PVC) the halogen acts as a flame retardant in the
event of combustion and prevents complete burning of the plastic.
If there is as filler mixed with the compound which is endothermic this
assists with the fire retardant effect of the compound.
Ein Mittel wird zur Verfügung gestellt, die Mittel von intumescence bei den Temperaturen über 195.degree habend. C. zu 220.degree. C. Das Mittel ist ein anschwellendes Puder, das durch die molaren Verhältnisse (2.20 bis 3.70) definiert wird SiO.sub.2 /(0.20 zu 0.35) Li.sub.2 O: (0.65 zu 0.80)(Na.sub.2 O+K.sub.2 O) wo die Koeffizienten von Li.sub.2 O und von (Na.sub.2 O+K.sub.2 O) Gesamtmenge 1.00 und thermoplastisches Material, das einen Plastikzustand an kleiner als 195.degree hat. C. Wenn das thermoplastische ein Halogen enthält, wie Polyvinylchlorverbindung (PVC) die Halogentaten als flammhemmendes im Falle der Verbrennung und das komplette Brennen des Plastiks verhindert. Wenn es als Füller gibt, der mit dem Mittel gemischt wird, das endothermisch ist, dieses unterstützt mit dem feuerverzögernden bewirken vom Mittel.