A method is disclosed for directly preparing alkali metal aluminum hydrides
such as NaAlH.sub.4 and Na.sub.3 AlH.sub.6 from either the alkali metal or
its hydride, and aluminum. The hydride thus prepared is doped with a small
portion of a transition metal catalyst compound, such as TiCl.sub.3,
TiF.sub.3, or a mixture of these materials, in order to render them
reversibly hydridable. The process provides for mechanically mixing the
dry reagents under an inert atmosphere followed by charging the mixed
materials with high pressure hydrogen while heating the mixture to about
125.degree. C. The method is relatively simple and inexpensive and
provides reversible hydride compounds which are free of the usual
contamination introduced by prior art wet chemical methods.
Een methode wordt onthuld voor direct het voorbereiden van de hydriden van het alkalimetaalaluminium zoals NaAlH.sub.4 en Na.sub.3 AlH.sub.6 van of het alkalimetaal of zijn hydride, en aluminium. Het zo voorbereide hydride wordt gesmeerd met een klein gedeelte van een de katalysatorsamenstelling van het overgangsmetaal, zoals TiCl.sub.3, TiF.sub.3, of een mengsel van deze materialen om hen omkeerbaar hydridable te maken. Het proces voorziet mechanisch het mengen van de droge reagentia onder een inerte atmosfeer die door de gemengde materialen met hoge drukwaterstof wordt gevolgd te belasten terwijl ongeveer het verwarmen van het mengsel aan 125.degree. C. De methode is vrij eenvoudig en goedkoop en verstrekt omkeerbare hydridesamenstellingen die van de gebruikelijke verontreiniging die door vroegere kunst natte chemische methodes vrij zijn wordt geïntroduceerd.