The invention provides a process for the production of amorphous silica
from a silica-based material having a silica content of at least 90%
comprising: a) heating said silica-based material with CaCl.sub.2, at a
temperature in the range of about 900.degree. C. to about 1,200.degree. C.
and in the presence of water vapor in excess of the stoichiometric amount
needed for the reaction: x CaCl.sub.2 +y SiO.sub.2 +x H.sub.2
O.fwdarw.(CaO).sub.x.multidot.(SiO.sub.2).sub.y +2x HCl wherein x is equal
to or greater than y to obtain a conversion of said silica-based material
to calcium silicates in excess of 99.9%; b) Leaching said calcium
silicates with HCl to form a solution of CaCl.sub.2 with insoluble silica;
c) separating said insoluble silica from solution; and d) recycling the
CaCl.sub.2 solution from step "c" to step "a".
A invenção fornece um processo para a produção do silicone amorfo de um material silicone-baseado que tem um índice do silicone ao menos de 90% que compreendem: a) aquecendo o material silicone-baseado dito com CaCl.sub.2, em uma temperatura na escala aproximadamente de 900.degree. C. aproximadamente a 1,200.degree. C. e na presença do vapor de água no excesso da quantidade stoichiometric necessitada para a reação: x CaCl.sub.2 +y SiO.sub.2 +x H.sub.2 O.fwdarw.(CaO).sub.x.multidot.(SiO.sub.2).sub.y +2x HCl wherein x é igual ou mais grande do que a y obter uma conversão de material silicone-baseado dito aos silicatos do cálcio em um excesso de 99.9%; b) Leaching silicatos ditos do cálcio com HCl para dar forma a uma solução de CaCl.sub.2 com silicone insoluble; c) separando silicone insoluble dito da solução; e d) recycling a solução CaCl.sub.2 da etapa "c" à etapa "a".