Carbon fiber bundles may be dispersed into substantially single
mono-filaments in pitch by stirring a mixture of fibers and pitch at a
temperature at which the pitch has a viscosity of about 0.1 to about 5
poise. The resulting fiber pitch binder contains about 0.5 to about 10.0
wt. % carbon fibers substantially dispersed as substantially single
mono-filaments which are randomly oriented which may then be used directly
as a binder for producing carbon bodies, for example, graphite electrodes,
pinstock or specialty graphite articles. This unique binder using an
economical amount of carbon fibers has the capacity to increase the
strength and reduce the coefficients of thermal expansion of the resulting
carbon products in more than one direction due to the random orientation
of the carbon fibers.
Carbonfaserbündel können in im wesentlichen einzelne Einzelheizfäden im Taktabstand, indem man eine Mischung der Fasern und rührt im Taktabstand bei einer Temperatur zerstreut werden, bei der der Taktabstand eine Viskosität von ungefähr 0.1 zu Poise ungefähr 5 hat. Die resultierende Fasertaktabstand Mappe enthält ungefähr 0.5 zu ungefähr 10.0 Gew.% Carbon-Fasern, die im wesentlichen als im wesentlichen einzelne Einzelheizfäden zerstreut werden, die nach dem zufall orientiert werden, das direkt als Mappe für das Produzieren der Carbonkörper, z.B., der Graphitelektroden, des pinstock oder der Spezialgebiet Graphitartikel dann verwendet werden kann. Diese einzigartige Mappe, die eine ökonomische Menge Carbonfasern verwendet, hat die Kapazität, die Stärke zu erhöhen und die Wärmeausdehnungkoeffizienten der resultierenden Carbonprodukte in mehr als einer Richtung zu verringern wegen der gelegentlichen Lagebestimmung der Carbonfasern.