An aerogel type platinum-ruthenium-carbon catalyst of microporous structure
maintaining long-term high catalytic activity, suitable for a direct
methanol fuel cell, is manufactured by a sol-gel process, and
supercritical drying while maintaining a microporous structure. The
catalyst contains 5 to 70% by weight of platinum and ruthenium, remainder
carbon, the platinum and ruthenium atomic ratio being of 1/4 to 4/1. Metal
salts and base catalyst are added to a solution of organic gel materials,
a solution of basic amine is added to the first solution, and the pH of
the resulting solution is adjusted forming a sol, the sol is aged at 40 to
90 for 1 to 20 days forming and stabilizing the gel, solvent is removed
from the gel by supercritical drying, and finally the aerogel is
carbonized in an inert atmosphere, followed by hydrogen reduction.
Un tipo catalizzatore del aerogel del platino-rutenio-carbonio della struttura microporosa che effettua l'alta attività catalitica di lunga durata, adatto a cellula di combustibile diretta del metanolo, è prodotto da un processo del solenoide-gel e da un essiccamento ipercritico mentre effettua una struttura microporosa. Il catalizzatore contiene 5 - 70% a peso di platino e rutenio, carbonio di resto, il platino e rapporto atomico del rutenio che sono di 1/4 - 4/1. I sali del metallo ed il catalizzatore basso sono aggiunti ad una soluzione dei materiali organici del gel, una soluzione dell'ammina di base è aggiunta alla prima soluzione ed il pH della soluzione risultante è registrato che forma un solenoide, il solenoide è invecchiato a 40 - 90 per 1 - 20 giorni che formano e che stabilizzano il gel, il solvente è rimosso dal gel da essiccamento ipercritico ed infine il aerogel è carbonizzato in un atmosfera inerte, seguito da riduzione dell'idrogeno.