Disclosed is the provision of a non-aging, highly anti-seed and
anti-black-speck steel plate for enameling without relying upon
decarbonization-denitrification annealing involving increased production
cost, and without the addition of expensive elements, such as niobium and
titanium involving increased alloying cost. This steel plate is produced
by adopting a steel composition comprising, by weight, carbon: not more
than 0.0018%, silicon: not more than 0.020%, manganese: 0.10 to 0.30%,
phosphorus: 0.010 to 0.030%, sulfur: not more than 0.030%, aluminum: not
more than 0.005%, nitrogen: 0.0008 to 0.0050%, boron: not more than
0.0050% and not less than 0.6 time the nitrogen content, and oxygen: 0.010
to 0.05%, and regulating the chemical composition of the steel and
regulating mainly hot rolling conditions to regulate the form of nitrides.
Se divulga la disposición de un no-envejecimiento, altamente contra-semilla y placa de acero de la contra-negro-mota para esmaltar sin confiar en el recocido de la descarbonizacio'n-desnitrificacio'n que implica coste de producción creciente, y sin la adición de elementos costosos, tales como niobium y titanio que implican coste de aleación creciente. Esta placa de acero es producida adoptando una composición de acero que abarca, por el peso, carbón: no más que 0.0018%, silicio: no más que 0.020%, manganeso: 0.10 a 0.30%, fósforo: 0.010 a 0.030%, sulfuro: no más que 0.030%, aluminio: no más que 0.005%, nitrógeno: 0.0008 a 0.0050%, boro: no más que 0.0050% y no no menos que 0.6 vez el contenido del nitrógeno, y oxígeno: 0.010 a 0.05%, y regulación de la composición química del acero y regulación principalmente de condiciones del balanceo caliente para regular la forma de nitruros.