The invention relates to an in-line process for producing high-temperature
stable glass. A sizing composition is advantageously used to reduce
plasticizing between the resinous matrix and the glass fibers. The in-line
process uses a melter or furnace apparatus, including a top charging and
melting section and an intermediate flow regulator section having a baffle
system improving the heat pattern across the glass flow, and a bushing
having a tip plate for receiving molten glass from a furnace. The bushing
has an enlarged size that allows drawing of a significantly increased
number of glass fibers at one time. The fibers have essentially no
catenary and may be wound to create a tightly wrapped package of glass
fibers of uniform exterior diameter throughout their width. High-strength,
high-silica fiber made according to the invention may be advantageously
used in filament-winding, pultrusion and weaving processes.
Η εφεύρεση αφορά μια ευθύγραμμη διαδικασία για το υψηλής θερμοκρασίας σταθερό γυαλί. Μια σύνθεση ταξινόμησης χρησιμοποιείται ευνοϊκά για να μειώσει την πλαστικοποίηση μεταξύ της ρητινούχης μήτρας και των ινών γυαλιού. Η ευθύγραμμη διαδικασία χρησιμοποιεί μια συσκευή melter ή φούρνων, συμπεριλαμβανομένου του χρεώνοντας και λειώνοντας τμήματος κορυφών και ένα ενδιάμεσο τμήμα ρυθμιστών ροής που έχει ένα σύστημα διαφραγμάτων που βελτιώνει το σχέδιο θερμότητας πέρα από τη ροή γυαλιού, και έναν δακτύλιο που έχει ένα πιάτο ακρών για τη λήψη του λειωμένου γυαλιού από έναν φούρνο. Ο δακτύλιος έχει ένα διευρυμένο μέγεθος που επιτρέπει το σχέδιο ενός σημαντικά αυξανόμενου αριθμού ινών γυαλιού συγχρόνως. Οι ίνες δεν έχουν ουσιαστικά καμία αλυσοειδή καμπύλη και μπορούν να τυλιχτούν για να δημιουργήσουν μια στενά τυλιγμένη συσκευασία των ινών γυαλιού της ομοιόμορφης εξωτερικής διαμέτρου σε όλο το πλάτος τους. Η υψηλής αντοχής, ίνα υψηλός-πυριτίου που γίνεται σύμφωνα με την εφεύρεση μπορεί να χρησιμοποιηθεί ευνοϊκά στις διαδικασίες ίνα-τυλίγματος, pultrusion και ύφανσης.