A fire-retardant wood-based composite is formed by treating a green wood
furnish with an amount of a phosphate/borate fire retardant treatment
effective to increase the fire retardancy of the resulting wood-based
composite, compared to the fire retardancy of the corresponding wood-based
composite lacking the fire retardant. The fire retardant treated green
wood furnish is blended with a binder and then bound, as by pressing the
furnish, to form a non-leaching fire-retardant wood based composite.
Another aspect of the invention is the product formed according to the
preceding process. The fire retardant may also act as a catalyst to cure
the binder and thus promote binding. Also, the addition of the fire
retardant to green wood chips, without the need to dry them to a low
moisture content, is believed to be novel.
Огнезамедлительная wood-based смесь сформирована путем обрабатывать зеленую древесину обеспечивает с количеством обработки пожара phosphate/borate retardant эффективной для того чтобы увеличить retardancy пожара приводя к wood-based смеси, сравненное к retardancy пожара соответствуя wood-based смеси нуждаясь retardant пожара. Пожар retardant обработанная зеленая, котор древесина обеспечивает смешан с связывателем и после этого прыгнут, как путем отжимать обеспечение, для того чтобы сформировать нон-vy5elaciva4 огнезамедлительной смесь основанную древесиной. Другим аспектом вымысла будет продукт сформированный согласно предшествующему процессу. Retardant пожара может также подействовать по мере того как катализатор для того чтобы вылечить связыватель и таким образом повысить связать. Также, поверены, что будет добавление retardant пожара для того чтобы позеленеть деревянные щепки, без потребности высушить их к содержанию низкой влаги, роман.