A conductive, moldable composite material for the manufacture of
electrochemical cell components comprising a thermosetting resin system
and conductive filler wherein the thermosetting resin composition
comprises: (1) a polybutadiene or polyisoprene resin; (2) an optional
functionalized liquid polybutadiene or polyisoprene resin; (3) an optional
butadiene- or isoprene-containing copolymer; and (4) an optional low
molecular weight polymer. In a preferred embodiment, the conductive
moldable composite material is used to form a bipolar plate, current
collector or other electrochemical cell component. Articles made of the
conductive moldable composite material are resistant to chemical attack
and hydrolysis, have excellent mechanical strength and toughness, have a
volume resistivity of about 0.116 ohm-cm or less and preferably about 0.04
ohm-cm or less and a thermal conductivity of at least about 5 watts/meter
.degree. K.
Ένα αγώγιμο, moldable σύνθετο υλικό για την κατασκευή των ηλεκτροχημικών τμημάτων κυττάρων που περιλαμβάνει ένα thermosetting σύστημα ρητίνης και ένα αγώγιμο υλικό πληρώσεως όπου η thermosetting σύνθεση ρητίνης περιλαμβάνει: (1) μια polybutadiene ή polyisoprene ρητίνη (2) ένας προαιρετικός η υγρή polybutadiene ή polyisoprene ρητίνη (3) ένα προαιρετικό βουταδιένιο - ή ησοπρενε-περιέχοντας copolymer και (4) ένα προαιρετικό χαμηλό πολυμερές σώμα μοριακού βάρους. Σε μια προτιμημένη ενσωμάτωση, το αγώγιμο moldable σύνθετο υλικό χρησιμοποιείται για να διαμορφώσει ένα διπολικό πιάτο, έναν τρέχοντα συλλέκτη ή άλλο ηλεκτροχημικό τμήμα κυττάρων. Τα άρθρα φιαγμένα από αγώγιμο moldable σύνθετο υλικό είναι ανθεκτικά στη χημικές επίθεση και την υδρόλυση, έχουν την άριστη μηχανική δύναμη και η ανθεκτικότητα, έχει μια ειδική αντίσταση όγκου περίπου 0,116 ωμ-εκατ. ή λιγότερων και κατά προτίμηση περίπου 0,04 ωμ-εκατ. ή λιγότερων και μια θερμική αγωγιμότητα τουλάχιστον περίπου 5 Watt/metriti's δεγρεε. Κ.