The invention includes a thin film optical coating having a layer
comprising sol-gel derived niobium oxide which is capable of providing an
index of refraction of at least about 1.90. The invention also includes a
thin film optical coating having a layer comprising a sol-gel derived
oxide system including niobium oxide and a second oxide component such as
aluminum oxide and/or silicon oxide which is capable of providing an index
of refraction of from about 1.60 to about 1.90. Also included in the
present invention are processes for producing such thin film coatings. In
the processes, a substrate is immersed in a mixture comprising niobium
chloride and an alcohol, withdrawn from the mixture, and heat-treated. The
mixture may also include aluminum precursors and/or silicon precursors.
The heat-treatment may occur at various temperatures, including those
under 200.degree. C.
L'invention inclut un enduit optique de la couche mince ayant une couche comporter l'oxyde de niobium dérivé pargel qui est capable de fournir un indice de réfraction au moins environ de 1.90. L'invention inclut également un enduit optique de la couche mince ayant une couche comporter un système d'oxyde dérivé pargel comprenant l'oxyde de niobium et un deuxième composant d'oxyde tel que l'oxyde d'aluminium et/ou l'oxyde de silicium qui est capable de fournir un indice de réfraction de environ de 1.60 environ à 1.90. En outre inclus dans la présente invention sont des procédés pour produire de tels enduits de la couche mince. Dans les processus, un substrat est immergé dans un mélange comportant le chlorure de niobium et un alcool, retiré du mélange, et soumis à un traitement thermique. Le mélange peut également inclure les précurseurs en aluminium et/ou les précurseurs de silicium. Le traitement thermique peut se produire aux diverses températures, y compris ceux sous 200.degree. C.