The present invention relates to a method for preparing nano-level Pt/C
electrocatalyst for cathode of fuel cell. By employing ammonium chloride,
potassium chloride, ammonium bromide, potassium bromide, ammonium iodide
or potassium iodide as anchoring agent for the chloroplatinic acid, the
present invention realizes the preparation of Pt/C electrocatalyst with
platinum micro-particles homogeneously distributed in the interstices as
well as on the surfaces of the active carbon. The sizes of the platinum
particles in the catalyst are homogeneous and their average diameter is in
the range of 2.5 to 4.5 mm. The present method is a novel one for
preparing nanometer level Pt/C electrocatalyst. Said electrocatalyst
possesses high specific activity per unit mass for the catalytic reduction
of oxygen.
Присытствыющий вымысел относит к методу для подготовлять electrocatalyst нано-urovn4 Pt/C для катода топливного элемента. Путем использовать хлорид аммония, хлорид калия, бромид аммония, бромид калия, иодид аммония или иодид калия как ставить вещество на якорь для chloroplatinic кислоты, присытствыющий вымысел осуществляет подготовку electrocatalyst Pt/C при микрочастицы платины однотипово распределенные в межузлиях также,как на поверхности активно углерода. Размеры частиц платины в катализаторе однотиповы и их средний диаметр находится в ряде от 2.5 до 4.5 миллиметров. Действующим сегодня методом будет роман одно для подготовлять electrocatalyst уровня Pt/C нанометра. Сказанное electrocatalyst обладает высокой специфически деятельностью в массу блока для каталитического уменьшения кислорода.