It is an object of the present invention to provide a thermoplastic
elastomer composition excellent in softness, permanent compression set
(both short- and long-term) and resistance to oil, and controlled in
bleed-out of the softening agent. It is another object of the present
invention to provide a formed article and composite formed article of the
above thermoplastic elastomer composition. The present invention provides
a thermoplastic elastomer composition containing (a) 100 parts by weight
of at least one hydrogenated block copolymer, (b) 30 to 150 parts by
weight of a non-aromatic-based softening agent for rubber and (c) 3 to 100
parts by weight of a thermoplastic resin having a melting point of 70 to
140.degree. C., determined by the DSC analysis, and melt viscosity of 400
to 100,000 cps at 140.degree. C., and formed article and composite formed
article thereof.
Es un objeto de la actual invención para proporcionar una composición termoplástica del elastomer excelente en suavidad, la compresión permanente fijada (corto y largo plazo) y la resistencia al aceite, y controlado en sangre -hacia fuera del agente que ablanda. Es otro objeto de la actual invención para proporcionar un artículo formado y el artículo formado compuesto de la composición termoplástica antedicha del elastomer. La actual invención proporciona una composición termoplástica del elastomer que contiene (a) 100 porciones en peso de por lo menos un copolímero hidrogenado del bloque, piezas de (b) 30 a 150 en peso de un agente que ablanda no-aroma'tico-basado para el caucho y las piezas de (c) 3 a 100 en peso de una resina termoplástica que tiene un punto de fusión de 70 a 140.degree. C., determinada por el análisis de DSC, y viscosidad del derretimiento de 400 a 100.000 CPS en 140.degree. C., y artículo formado formado del artículo y compuesto de eso.