This invention is based upon the unexpected finding that random copolymers
of 1,3-butadiene monomer and 3-(2-pyrrolidinoethyl) styrene and/or
4-(2-pyrrolidinoethyl) styrene having a low vinyl content can be
synthesized by anionic polymerization at normal polymerization
temperatures without the need for a conventional polar modifier. The
subject invention more specifically discloses a process for synthesizing a
rubbery polymer that comprises copolymerizing at least one conjugated
diolefin monomer and at least one functionalized monomer in an organic
solvent at a temperature which is within the range of 20.degree. C. to
about 100.degree. C., wherein the polymerization is initiated with an
anionic initiator, wherein the functionalized monomer is of the structural
formula:
##STR1##
wherein n represents an integer from 4 to about 10, and wherein the
polymerization is conducted in the absence of conventional polar
modifiers.
Cette invention est basée sur l'inattendu constatant que des copolymères aléatoires du monomère 1,3-butadiene et 3-(2-pyrrolidinoethyl) du styrène et/ou 4-(2-pyrrolidinoethyl) du styrène ayant un bas contenu de vinyle peuvent être synthétisés par polymérisation anionique aux températures normales de polymérisation sans besoin de modificateur polaire conventionnel. L'invention soumise révèle plus spécifiquement un procédé pour synthétiser un polymère caoutchouteux qui comporte copolymerizing au moins un monomère conjugué d'dioléfine et au moins on functionalized le monomère dans un dissolvant organique à une température qui est dans la marge de 20.degree. C. environ à 100.degree. C., où la polymérisation est lancée avec un initiateur anionique, où functionalized le monomère est de la formule structurale : ## du ## STR1 où n représente un nombre entier de 4 environ à 10, et où la polymérisation est conduite en l'absence des modificateurs polaires conventionnels.