A lithium secondary battery having improved load characteristics such as
high rate discharge properties is obtained by using a mixed cathode active
material comprising a mixture of lithium-containing manganese oxide having
a spinel type crystal structure and lithium-containing cobalt oxide,
wherein the cathode collector retains mixed cathode active material in
such a manner that the mixing ratio of lithium cobaltate X thereof should
fall in a range of 0.1.ltoreq.X.ltoreq.0.9, that the bulk density Y
(g/cm.sup.3) of the cathode mixed agent should be confined in a range
satisfying the relation of 0.5X+2.7.ltoreq.Y.ltoreq.0.6X+3.3, and that the
mean particle diameter of spinel type lithium manganate should be greater
than the mean particle diameter of lithium cobaltate.
Una batteria secondaria del litio che migliora le caratteristiche del carico quali le proprietà di scarico di alto tasso è ottenuta usando un materiale attivo del catodo mixed che contiene una miscela l'ossido litio-contenente del manganese che ha un tipo spinel struttura di cristallo e checontiene l'ossido del cobalto, in cui il collettore del catodo mantiene il materiale attivo del catodo mixed in maniera tale che il rapporto di miscelazione del cobaltate X del litio di ciò dovrebbe cadere in una gamma di 0.1.ltoreq.X.ltoreq.0.9, che la densità all'ingrosso Y (g/cm.sup.3) dell'agente mescolato catodo dovrebbe essere limitata in una gamma che soddisfa il rapporto di 0.5X+2.7.ltoreq.Y.ltoreq.0.6X+3.3 e che il diametro medio della particella di tipo spinel manganato del litio dovrebbe essere più grande del diametro medio della particella del cobaltate del litio.