The present invention relates to solvent-free, NCO prepolymers having a
residual IPDI monomer content of less than 2.0 wt. %, an NCO content of
2.0 to 5.0 wt. % and a viscosity of 5000 to 20,000 mPa.multidot.s, wherein
the NCO prepolymers are the reaction products of
i) 3-isocyanatomethyl-3,5,5-trimethylcyclohexyl isocyanate and
ii) one or more polyethers prepared by the DMC catalyst process and having
an OH-functionality of 1.80 to 2.00
at an NCO/OH equivalent ratio of 1.5:1 to 2.2:1.
The present invention also relates to a process for preparing these
solvent-free, NCO prepolymers and to polyurethane coating, sealant,
adhesive and/or embedding compositions containing the solvent-free, NCO
prepolymers as a binder and/or binder component.
La actual invención se relaciona con los prepolymers sin solvente, del NCO que tienen un contenido residual del monomer de IPDI de menos de 2.0 pesos %, un contenido del NCO de 2.0 a 5.0 pesos % y una viscosidad de 5000 a 20.000 mPa.multidot.s, en donde los prepolymers del NCO son los productos de la reacción i) del isocianato de 3-isocyanatomethyl-3,5,5-trimethylcyclohexyl e ii) unos o más polyethers se prepararon el proceso del catalizador de DMC y teniendo una OH-funcionalidad de 1.80 a 2.00 en un cociente equivalente de NCO/OH de 1.5:1 a 2.2:1. La actual invención también se relaciona con un proceso para preparar estos prepolymers sin solvente, del NCO y con la capa del poliuretano, el sellante, adhesivo y/o encajar las composiciones que contienen los prepolymers sin solvente, del NCO como una carpeta y/o componente de la carpeta.