Aluminium hydroxide of high whiteness is produced by (i) heating aluminium
hydroxide obtained from the Bayer process to a temperature of 300 to
700.degree. C. (ii) dissolving the soluble fraction of the thus obtained
activated product at 85 to 275.degree. C. in aqueous sodium hydroxide to
form a sodium aluminate liquor containing an undissolved residue of very
fine boehmite, (iii) filtering said sodium aluminate liquor to obtain a
clear solution of sodium aluminate supersaturated with respect to
dissolved alumina, (iv) cooling said clear solution to 50 to 80.degree. C.
and seeding with crystallized aluminium hydroxide to induce further
crystallization, and (v) separating, washing and drying the produced
aluminium hydroxide crystals.
Aluminiumhydroxid der hohen Weiße wird durch (i) das Heizung Aluminiumhydroxid produziert, das aus dem Bayer Prozeß zu einer Temperatur von 300 zu 700.degree erhalten wird. C. (ii), das den löslichen Bruch des folglich erreichten aktivierten Produktes bei 85 zu 275.degree auflöst. C. im wäßrigen Natriumhydroxid, zum eines Natriumaluminatalkohols zu bilden, der einen unaufgelösten Überrest des sehr feinen boehmite, (iii) filternder besagter Natriumaluminatalkohol enthält, um eine freie Lösung des Natriumaluminats zu erreichen übersättigt in Bezug auf aufgelöste Tonerde, (iv) abkühlende besagte freie Lösung bis 50 zu 80.degree. C. und säend mit kristallisiertem Aluminiumhydroxid, um weitere Kristallisation zu verursachen und (V), die produzierten Aluminiumhydroxidkristalle trennend, waschend und trocknend.