The present invention relates to poly .alpha.-olefins (PAO's) which exhibit
superior Noack volatility at low pour points. Mixtures of 1-decene and
1-dodecene are polymerized using an alcohol promoted BF.sub.3 in
conjunction with a combination of cocatalysts. The reaction mixture is
distilled to remove the unreacted monomeric and dimeric species. The
resulting product is then hydrogenated to saturate the oliogomers to
provide a hydrogenated product which has a viscosity of 5 cSt. This
product is distilled to provide PAO's of varying viscosity grades. The 4
cSt PAO is comprised mostly of trimers and tetramers while the 6 cSt
product is comprised of trimers, tetramers, and pentamers.
La présente invention concerne les poly alpha.-oléfines (PAO) qui montrent la volatilité supérieure de Noack au bas des points de congélation. Des mélanges de 1-decene et de 1-dodecene sont polymérisés en utilisant un BF.sub.3 favorisé par alcool en même temps qu'une combinaison des cocatalysts. Le mélange de la réaction est distillé pour enlever les espèces monomériques et dimères non réagies. Le produit résultant est alors hydrogéné pour saturer les oliogomers pour fournir un produit hydrogéné qui a une viscosité de la rue 5. Ce produit est distillé pour fournir PAO des viscosités variables. 4 La rue PAO est composée la plupart du temps des trimères et des tétramères tandis que le produit de la rue 6 est composé des trimères, des tétramères, et des pentamères.