After coating a hydrogen absorbing alloy slurry obtained by kneading a
hydrogen absorbing alloy powder 12a, a polyethylene oxide (PEO) powder as
a binder 12b, and a suitable amount of water (a solvent for binder) to
both surfaces of a metal core plate (active material holder) made of a
punching metal, the core plate is dried. Then, after removing the active
material layer 13 from the core plate 11 by a means such as cutting and
the like, a definite amount of water (a solvent for binder) is sprayed to
the cut surface (the exposed surface of the core plate 11) to attach the
water to the cur surface followed by drying to provide a hydrogen
absorbing alloy electrode 10, which is disposed at the outermost side of
the electrode group.
Após ter revestido uma pasta absorvente da liga do hidrogênio obtida kneading um pó absorvente 12a da liga do hidrogênio, um pó do óxido do polietileno (PEO) como uma pasta 12b, e uma quantidade apropriada da água (um solvente para a pasta) a ambas as superfícies de uma placa do núcleo do metal (suporte material ativo) feita de um metal perfurando, a placa do núcleo são secados. Então, após ter removido a camada material ativa 13 da placa 11 do núcleo pelo os meios tais como o corte e o gosto, uma quantidade definitiva da água (um solvente para a pasta) são pulverizados à superfície do corte (a superfície exposta da placa 11 do núcleo) para unir a água à superfície do cur seguida secando para fornecer um elétrodo absorvente 10 da liga do hidrogênio, que seja disposto no lado outermost do grupo do elétrodo.