Tin is added to a zinc cathode target to enhance the sputter efficiency of
the target. Films deposited using the cathode, e.g., greater than zero but
less than 10 weight percent tin and greater than 90 but less than 100
weight percent zinc improve the chemical durability of a high
transmittance, low emissivity coating stack over coating stacks having
zinc oxides without tin oxide. High transmittance, low emissivity coating
stacks are heated with the heated coating having reduced haze by selecting
the thickness of metal primer layer between an infrared reflective film,
e.g. a silver film and a dielectric film, e.g., a 52-48 zinc stannate,
zinc oxide, tin oxide film or a zinc oxide film. Also disclosed are
enhancing films that lower the resistivity of silver films deposited
thereon and improve chemical durability of the coating stack.
La latta è aggiunta ad un obiettivo del catodo dello zinco per aumentare l'efficienza di polverizzazione dell'obiettivo. Le pellicole hanno depositato per mezzo del catodo, per esempio, una latta da più notevolmente di zero ma più meno di 10 percento del peso e più notevolmente di 90 ma uno zinco da più meno di 100 percento del peso migliora la durevolezza chimica di alta trasmissione, pile eccessive del rivestimento di emissività della pila bassa del rivestimento che hanno ossidi dello zinco senza ossido della latta. L'alta trasmissione, pile basse del rivestimento di emissività è riscaldata con il rivestimento riscaldato che riduce l'opacità selezionando lo spessore dello strato dell'iniettore del metallo fra una pellicola riflettente infrarossa, per esempio una pellicola d'argento e una pellicola dielettrica, per esempio, uno stannate dello zinco 52-48, ossido dello zinco, pellicola dell'ossido della latta o una pellicola dell'ossido dello zinco. Inoltre rilevato stanno aumentando le pellicole che abbassano la resistività delle pellicole d'argento depositate su ciò e migliorano la durevolezza chimica della pila del rivestimento.