A polymer dispersion is prepared by copolymerization of from 20 to 70 parts
by weight of a monomer mixture comprising
a) from 2.5 to 100% by weight of one or more (meth)acrylates of monohydric,
saturated C.sub.3 -C.sub.8 -alcohols as monomers A and
b) from 0 to 97.5% by weight of one or more further ethylenically
unsaturated monomers as monomers B
in 100 parts by weight of an aqueous solution which contains from 5 to 35%
by weight of a starch or of a starch derivative by emulsion polymerization
in the presence of an initiator containing peroxide groups, by a process
in which the initiator and monomers are metered in continuously and
wherein, a first amount of initiator is metered in over a first feed
period of from 5 to 60 minutes and a second amount of initiator is metered
in over a second feed period of from 15 to 180 minutes, the first amount
of initiator being greater than the second amount of initiator.
Uma dispersão do polímero é preparada pelo copolymerization de 20 a 70 porções pelo peso de uma mistura do monomer que compreende a) de 2.5 a 100% pelo peso de um ou de mais (meth)acrylates de C.sub.3 monohydric, saturated - C.sub.8 - álcoois como os monomers A e b) de 0 a 97.5% por um peso de um ou mais monomers ethylenically unsaturated mais adicional como os monomers B em 100 porções pelo peso de uma solução aqueous que contenha 5 a 35% pelo peso de um starch ou de um derivative do starch pela polimerização do emulsion na presença de um iniciador conter o peroxide agrupe, por um processo em que o iniciador e os monomers metered dentro continuamente e wherein, um primeiro uma quantidade de iniciador é excesso dentro metered um o primeiro período da alimentação de 5 a 60 minutos e uma segunda quantidade de iniciador é excesso dentro metered um segundo período da alimentação de 15 a 180 minutos, a primeira quantidade de iniciador que é mais grande do que a segunda quantidade de iniciador.