Alloyed galvanized steel plate having excellent slidability

   
   

An alloyed hot-dip galvanized steel sheet is obtained by forming a hot-dip galvanized layer on the surface of the steel sheet and then alloying the steel sheet. The steel sheet exhibits a potential of -850 mV or less when it is immersed in a zinc sulfate-sodium chloride electrolyte. Alternatively, when it is electrolyzed according to constant potential electrolysis process in a zinc sulfate-sodium chloride electrolyte at a potential in a range from -940 mV to -920 mV, the quantity of electricity consumed is less than or equal to 0.5 C/cm.sup.2. The steel sheet exhibits excellent processability and particularly excellent sliding property.

Сплавленное горяч-okunaet гальванизированный стальной лист получено путем формировать горяч-okunaet гальванизированный слой на поверхности стального листа и после этого сплавлять стальной лист. Стальной лист exhibits потенциал -850 mV или когда он погружен в электролите хлорида сульфат-natri4 цинка. Друг, когда оно электролизован согласно постоянн потенциальному процессу электролиза в электролите хлорида сульфат-natri4 цинка на потенциале в ряде от -940 mV до -920 mV, уничтоженное количество электричества less than or equal to 0.5 C/cm.sup.2. Стальной лист exhibits превосходное processability и определенно превосходное сползая свойство.

 
Web www.patentalert.com

< Duplex stainless steel

< Multicolored steel sheet manufacturing method and a multicolored steel sheet manufacturing system

> Stainless steel separator for fuel cells, method for making the same, and solid polymer fuel cell including the same

> Multi-layer steel cable for tire carcass

~ 00153