A process and apparatus for creating an acoustically absorbent porous panel
comprises the steps of dispensing cement and fibers with a dry mixer to
create a dry mix and aqueous mixing water, surfactant and air with an
aqueous mixer to create a foam. The process and apparatus provides for
combining and mixing the foam and dry mix in a combining mixer to form a
foamed cementitious material comprising on a wet basis about 53% to about
68% by weight cement, about 17% to about 48% by weight water, about 0.05%
to about 5% by weight fibers, and about 0.01% to about 10% by weight
surfactant. The foamed cementitious material is then dried or cured in a
drying chamber. The dried foamed cementitious material may then textured
with an embossing roller. The cementitious material provides good
acoustical performance with enhanced durability and moisture resistance.
Μια διαδικασία και μια συσκευή για μια ηχητικά απορροφητική πορώδη επιτροπή περιλαμβάνουν τα βήματα της διανομής του τσιμέντου και των ινών με έναν ξηρό αναμίκτη για να δημιουργήσουν ένα ξηρό μίγμα και ένα υδάτινο ύδωρ μίξης, ένα μέσο επιπολής και τον αέρα με έναν υδάτινο αναμίκτη για να δημιουργήσουν έναν αφρό. Η διαδικασία και η συσκευή προβλέπουν το συνδυασμό και τη μίξη του αφρού και του ξηρού μίγματος σε έναν αναμίκτη συνδυασμού για να διαμορφωθεί ένα αφρισμένο τσιμεντένιο υλικό περιλαμβάνοντας σε υγρή βάση για 53% σε περίπου 68% από το τσιμέντο βάρους, περίπου 17% σε περίπου 48% από το ύδωρ βάρους, περίπου 0,05% σε περίπου 5% από τις ίνες βάρους, και περίπου 0,01% σε περίπου 10% από το μέσο επιπολής βάρους. Το αφρισμένο τσιμεντένιο υλικό είναι έπειτα ξηρό ή θεραπευμένο σε μια ξεραίνοντας αίθουσα. Το ξηρό αφρισμένο τσιμεντένιο υλικό μπορεί έπειτα κατασκευασμένος με έναν κύλινδρο αποτύπωσης σε ανάγλυφο. Το τσιμεντένιο υλικό παρέχει στην καλή ακουστική εκτέλεση την ενισχυμένες διάρκεια και την αντίσταση υγρασίας.