The present invention relates to an oxide sintered body having a perovskite
structure represented with a chemical formula of MRuO.sub.3 (M: one or
more types among Ca, Sr, Ba), characterized in that the total content of
alkali metals such as Na, K, and Fe, Ni, Co, Cr, Cu, Al is 100 ppm or
less, the content of respective elements U, Th is 10 ppb or less, and the
relative density is 90% or more, and provides an oxide sintered body and
the manufacturing method thereof having a pervoskite structure represented
with the chemical formula MRuO.sub.3 (M: one or more types among Ca, Sr,
Ba) by using a MRuO.sub.3 sintered body raw material refined to a high
density of 4N or more, which enables sintering at low temperatures, and
which is capable of obtaining a high-density sintered body.
Η παρούσα εφεύρεση αφορά ένα συμπυκνωμένο οξείδιο σώμα που έχει μια perovskite δομή αντιπροσωπευμένη με έναν χημικό τύπο MRuO.sub.3 (μ: ένας ή περισσότεροι τύποι μεταξύ του ασβεστίου, του SR, του BA), που χαρακτηρίζονται δεδομένου ότι το συνολικό περιεχόμενο των αλκαλικών μετάλλων όπως το NA, το Κ, και το Φε, Νι, κοβάλτιο, χρώμιο, cu, Al είναι 100 PPM ή λιγότερος, το περιεχόμενο του αντίστοιχου u στοιχείων, θόριο είναι ppb 10 ή λιγότερος, και η σχετική πυκνότητα είναι 90% ή περισσότερος, και παρέχει σε ένα συμπυκνωμένο οξείδιο σώμα και τη μέθοδο κατασκευής επ' αυτού που έχουν μια δομή pervoskite αντιπροσωπευόμενη το χημικό τύπο MRuO.sub.3 (μ: ένας ή περισσότεροι τύποι μεταξύ του ασβεστίου 4N ή περισσότερος, ο οποίος επιτρέπει τη συμπύκνωση στις χαμηλές θερμοκρασίες, και που είναι σε θέση ένα υψηλής πυκνότητας συμπυκνωμένο σώμα.