The present invention provides novel low molecular weight, high
functionality number, polymers. The polymers may be made, for example, by
heating (preferably, to a temperature of between about 130.degree. C. and
180.degree. C.) one or more ethylenically unsaturated monomers in the
presence of a substantially aprotic solvent system; and maintaining the
temperature for a time sufficient to polymerize the monomers to a
preferred monomer to polymer conversion percentage of at least about 95
percent by weight. In a presently preferred embodiment, the polymer has a
weight average molecular weight between about 900 and 7,000 Dalton and a
functionality number of at least 100. The process is also preferably
substantially free of chain transfer agents.
Η παρούσα εφεύρεση παρέχει το νέο χαμηλό μοριακό βάρος, υψηλός αριθμός λειτουργίας, πολυμερή σώματα. Τα πολυμερή σώματα μπορούν να γίνουν, παραδείγματος χάριν, με τη θέρμανση (κατά προτίμηση, σε μια θερμοκρασία μεταξύ για 130.degree. Γ. και 180.degree. γ.) ένα ή περισσότερα αιθυλενικά ακόρεστα μονομερή παρουσία ενός ουσιαστικά απρωτονικού διαλυτικού συστήματος και διατηρώντας τη θερμοκρασία για έναν χρόνο επαρκή για να πολυμερίσει τα μονομερή σε ένα προτιμημένο μονομερές στο ποσοστό πολυμερούς μετατροπής τουλάχιστον περίπου 95 τοις εκατό από το βάρος. Σε μια προς το παρόν προτιμημένη ενσωμάτωση, το πολυμερές σώμα έχει ένα μέσο μοριακό βάρος βάρους μεταξύ περίπου 900 και 7.000 dalton και ενός αριθμού λειτουργίας τουλάχιστον 100. Η διαδικασία είναι επίσης κατά προτίμηση ουσιαστικά χωρίς πράκτορες μεταφοράς αλυσίδων.