The present invention provides an image-receiving sheet for
electrophotography, which is capable of providing an image excellent in
gloss and which has an excellent offset resistance during a fixing step at
a high temperature. The toner image-receiving layer comprises a polyester
resin having the following characteristic properties:
(1) said polyester resin containing at least 10%, based on the molar number
of the whole polyhydric alcohol components, of bisphenol A as a polyhydric
alcohol component;
(2) said polyester resin has an intrinsic viscosity of 0.30 to 0.70;
(3) said polyester resin has a flow-starting temperature of 100 to
160.degree. C.; and
(4) said polyester resin has a glass transition temperature ranging from
50.degree. C. to a temperature lower than the fixing temperature by
10.degree. C.
La présente invention fournit une feuille réceptrice d'images pour l'électrophotographie, qui est capable de fournir une image excellente dans le lustre et qui a une excellente résistance excentrée pendant une étape de réparation à température élevée. La couche réceptrice d'images de toner comporte une résine de polyester ayant les propriétés caractéristiques suivantes : (1) résine de polyester contenant au moins 10%, basé sur le nombre molaire de composants polyhydriques d'alcool de totalité, du bisphenol A comme composant polyhydrique d'alcool ; (2) la résine de polyester a une viscosité intrinsèque de 0.30 à 0.70 ; (3) la résine de polyester a une température couler-commençante de 100 à 160.degree. C. ; et (4) la résine de polyester a une température de transition de verre s'étendre de 50.degree. C. à une température inférieure à la température de réparation par 10.degree. C.