The present invention is to provide a high transmittance glass sheet that
has a composition containing as coloring components, expressed in wt. %,
0.005 to less than 0.02% of total iron oxide in terms of Fe.sub.2 O.sub.3,
less than 0.008% of FeO, and 0 to 0.25% of cerium oxide and having a ratio
of FeO in terms of Fe.sub.2 O.sub.3 to the total iron oxide of lower than
40%, and exhibits high visible light transmittance and solar radiation
transmittance. Alternatively, a high transmittance glass sheet is provided
that contains not more than 0.06% of total iron oxide and 0.025 to 0.20%
of cerium oxide and has a ratio of a fluorescence intensity at 395 nm to a
fluorescence intensity at 600 nm of 10% or higher when subjected to
ultraviolet irradiation at a wavelength of 335 nm.
Η παρούσα εφεύρεση είναι να παρασχεθεί ένα υψηλό φύλλο γυαλιού μετάδοσης που έχει μια σύνθεση που περιέχει ως χρωματισμό των συστατικών, που εκφράζονται στα βάρη %, 0,005 σε λιγότερο από 0,02% του συνολικού οξειδίου σιδήρου από την άποψη Fe.sub.2 O.sub.3, λιγότερο από 0,008% FeO, και 0 0,25% του οξειδίου δημήτριου και κατοχή μιας αναλογίας FeO από την άποψη Fe.sub.2 O.sub.3 στο συνολικό οξείδιο σιδήρου της χαμηλότερης από 40%, και υψηλής ορατής ελαφριάς μετάδοσης εκθεμάτων και ηλιακή μετάδοση ακτινοβολίας. Εναλλακτικά, ένα υψηλό φύλλο γυαλιού μετάδοσης παρέχεται που περιέχει όχι περισσότερο από 0,06% του συνολικού οξειδίου σιδήρου και 0,025 0,20% του οξειδίου δημήτριου και έχει μια αναλογία μιας έντασης φθορισμού σε 395 NM σε μια ένταση φθορισμού σε 600 NM 10% ή υψηλότερος όταν υποβάλλεται στην υπεριώδη ακτίνα ακτινοβολία μήκος κύματος 335 NM.