The invention relates to a process for trapping a free monomer which has
not reacted by copolymerization or by grafting comprising at least one
epoxide functional group in a thermoplastic composition based on ethylene
and/or on propylene and based on at least one monomer comprising at least
one epoxide functional group. The process can comprise the following
stages: (i) preparation of the thermoplastic composition; and (ii)
addition of a sufficient amount of a solid trapping additive exhibiting,
at its surface, sites with a basic nature within the Lewis or Bronstead
meaning. The trapping additive comprises a porous zeolite, the diameter of
the pores of which is between 5 and 15 angstroms, preferably between 6 and
13 angstroms. The invention also relates to the composition obtained by
such a process and to the blends comprising such a composition.
La invención se relaciona con un proceso para atrapar un monomer libre que no ha reaccionado por la copolimerización o injertando abarcando por lo menos un grupo funcional del epoxide en una composición termoplástica basada en el etileno y/o en el propylene y basada en por lo menos un monomer que abarcaba por lo menos un grupo funcional del epoxide. El proceso puede abarcar las etapas siguientes: (i) preparación de la composición termoplástica; y (ii) adición de una suficiente cantidad de una interceptación sólida aditiva exhibiendo, en su superficie, sitios con una naturaleza básica dentro del significado de Lewis o de Bronstead. El añadido de la interceptación abarca una zeolita porosa, el diámetro de los poros de la cual está entre 5 y 15 angstromes, preferiblemente entre 6 y 13 angstromes. La invención también se relaciona con la composición obtenida por tal proceso y con las mezclas que abarcan tal composición.