The present invention provides a cast steel for ring-shaped components that
has a low average coefficient of thermal expansion in a temperature range
of 20.degree. C. to 500.degree. C. and high strength and good oxidation
resistance at 500.degree. C., which are required for ring-shaped
components for use as blade rings and seal ring retainers of gas turbines,
and that can hence be used for blade rings and seal ring retainers of gas
turbines. Specifically, the present invention provides a high-strength and
low-thermal expansion cast steel comprising, on a mass percentage basis,
0.1 to 0.8% of C, 0.1 to 1.0% of Si, 0.1 to 1.0% of Mn, 0.01 to 0.1% of S,
greater than 40% and up to 50% of Ni, not greater than 4% (inclusive of
0%) of Co, greater than 1.5% and up to 4% of Cr, 0.01 to 0.1% of Al, and
0.001 to 0.1% of Mg, the remainder being substantially Fe.
De onderhavige uitvinding verstrekt een gietvormstaal voor ringvormige componenten dat een lage gemiddelde coëfficiënt van thermische uitbreiding in een temperatuurwaaier van 20.degree. C. aan 500.degree. C. en hoge sterkte en goede oxydatieweerstand bij 500.degree. C. heeft, dat voor ringvormige componenten voor gebruik als bladringen en pallen van de verbindingsring van gasturbines wordt vereist, en die vandaar voor bladringen en de pallen van de verbindingsring van gasturbines kan worden gebruikt. Specifiek, verstrekt de onderhavige uitvinding een uitbreiding gegoten staal met hoge weerstand en laag-thermisch bestaand, op een basis van het massapercentage, uit 0,1 tot 0,8% van C, 0,1 tot 1,0% van Si, 0,1 tot 1,0% van Mn, 0,01 tot 0,1% van S, groter dan 40% en tot 50% van Ni, niet groter dan 4% (inclusief van 0%) van Co, groter dan 1,5% en tot 4% van Cr, 0,01 tot 0,1% van Al, en 0,001 tot 0,1% van Mg, de rest die wezenlijk Fe is.